技術支援 >> UL測試

Example : E130155(M)
Mtl Dsg Col MinTNK
mm		 UL94
Flame
Class		 Elec RTI
with
IMP		 Mech
w/o
IMP		 HWI HAI HVTR D495 CTI
1100F. 1101FA. A11 0.83 94HB 130 75 140 4 1 0 - -
1100FB. 1110F.
   1.57
 94HB 130 120 140 4 0 0 - -
1111FA. 1111FB
   3.12
 94HB 130 120 140 3 0 0 5 0
    6.1
 94HB 130 120 140 1 0 1 - -
1403G3 A11 0.76
 94V-0 130 130 140 4 0 4 - -
    1.57
 94V-0 130 130 140 3 0 2 - -
    3.18
 94V-0 130 130 140 2 0 3 6 3
1403G6 A11 0.76
 94V-0 130 130 140 3 0 1 - -
    1.57
 94V-0 130 130 140 2 0 1 - -
    3.18 94V-0 130 130 140 2 0 1 6 3
Polybutylene terephthalate (PBTP) inthe from of pellets.
Ranges of valuew per Performance Level Class (PLC)
  HWI
Hot Wire
lgnition		 HAI
High
ampere
arcignition		 HVTR
High voltage
arc tracking
rate		 D 495
Arc resistance.		 CTI
Comparative
tracking
Index
Unit
s number mm/min s
 v
Class 0
 ≥120 ≥120 0-10 ≥420 >600
Class 1 60-<120 60-<120 >10-25.4 360-<420 400-<600
Class 2 30-<60 30-<60 >25.4-80 300-<360 250-<400
Class 3 15-<30 15-<30 >80-150 240-<300 175-<250
Class 4 7-<15 0-<15 >150 180-<240 100-<175
Class 5 0-<7 - - 120-<180 0-<100
Class 6 - - - 60-<120 -
Class 7 - - - 0-<60 -
  • Mtl Dsg：原料名稱，如PBT、PC、ABS。
  • Col：顏色表示。All表示全部顏色；NC表示本色；BK表示黑色。
  • UL94 Flame Class：耐燃等級，分為5VA、V-0、V-1、V-2、HB。
  • >RTI：溫度指數(攝氏)，分電器與機械(有衝擊和無衝擊)，依照成品使用要求，溫度越高越佳。
  • HWI：熱導線著火試驗，通電流於電阻線圈，使期產生熱量，讓試片著火所需之時間(秒)。
  • >HAI：高安培電弧著火試驗，通高電流產生電弧測試幾次電弧後，使試片著火(次數)。
  • HVTR：高電壓電弧軌跡速率試驗，通高電壓產生電弧，一定時間電弧在試片上產生烙印之軌跡長度。(mm/min)
  • Arcd495：耐電弧測試(秒)。
  • CTI：相對軌跡指數，滴50滴特定溶液後，在試片表面通過電壓制產生勞痕所需之電壓(伏特)。